QuakeWrapR Carbon Plates
This table summarizes the properties of QuakeWrapR carbon plates; other products are available or can be developed to meet the specific project requirements.†
|
DU50C |
GU50C |
| Packaging |
3 inches wide |
4 inches wide |
| Fiber Orientation ‡ |
0 |
0 |
| Effective Thickness per Ply |
0.05 inch |
0.05 inch |
| Density, ASTM-D792 |
1.3 g/cm³ |
1.3 g/cm³ |
| Direction Tested (Long. or Trans.) |
L |
L |
| Maximum Load per Inch Width § |
15,400 lbs. |
20,300 lbs. |
| Tensile Strength, ASTM-D3039 |
309.0 ksi |
406.0 ksi |
| Modulus of Elasticity, ASTM-D3039 |
20,800 ksi |
23,900 ksi |
| Elongation at Failure |
1.5% |
1.5% |
Notes:
† The above results were obtained based on samples produced with two plies of fabric and under ideal laboratory conditions from a single lot. The average resin content of samples measured in accordance with ASTM-D2584 varied from 55% to 60% by weight. Due to variation in material properties from different lots, it is recommended that a strength reduction factor of 20% be applied to the above values.
‡ Unidirectional fabrics have negligible strength and stiffness in the transverse direction.
§ Values are reported for a single ply of fabric. Narrower width fabrics are available by special order.
|